Oriented thermoplastic films comprising polypropylene and poly(para-tertiary-butyl-styrene)

ABSTRACT

A resinous blend composition, adaptable for fabrication into an oriented film structure having improved physical properties comprising a polyolefin such as polypropylene containing incorporated therein additive amounts, on the order of from about 10 percent to about 40 percent by weight of a tertiary butyl substituted aromatic resin, such as poly(para-tertiary-butyl styrene).

United States Patent Bullard 51 May 30,1972

[54] ORIENTED THERMOPLASTIC FILMS COMPRISING POLYPROPYLENE AND POLY(PARA-TERTIARY-BUTYL- STYRENE) [72] Inventor: Edward M. Bullard, Rochester, NY.

[73] Assignee: Mobil Oil Corporation [22] Filed: July 29, 1970 [21] Appl. No.: 59,331

US. Cl. ..260/897 A, 264/289 3,092,891 6/1963 Baratti ..28/82 3,018,263 l/1962 Schneider. ..260/45.5 3,246,061 4/1966 Blatz ..264/95 Primary Examiner-Samuel H. Blech Assistant ExaminerC. J. Seccuro Attorney-Oswald G. Hayes, Andrew L. Gaboriault and James D. Tierney ABSTRACT A resinous blend composition, adaptable for fabrication into an oriented film structure having improved physical properties comprising a polyolefin such as polypropylene containing incorporated therein additive amounts, on the order of from about 10 percent to about 40 percent by weight of a tertiary butyl substituted aromatic resin, such as poly(para-tertiarybutyl styrene).

2 Claims, No Drawings ORIENTED THERMOPLASTIC FILMS COMPRISING POLYPROPYLENE AND POLY(PARA-TERTIARY- BUTYL-STYRENE) BACKGROUND OF THE INVENTION 1 Field of the Invention The present invention relates to resinous thermoplastic compositions adapted for use in the production of oriented thermoplastic film materials such as oriented polypropylene. Specifically, uncoated biaxially oriented films such as polypropylene have relatively high heat-sealing temperatures, in comparison to many other commercially available thermoplastic films such as, for example, polyethylene film, and have an extremely narrow heatseal range. Moreover, such oriented films exhibit a tendency to disorient, shrink, and tear when attempts are made to seal these films at their prerequisite heat-seal temperatures. In accordance with the present invention, additive amounts of poly(paratertiarybutyl styrene) on the order of from about percent up to about 40 percent by weight based upon the total weight of sample, are incorporated, utilizing conventional techniques, into polypropylene resins prior to the extrusion and orientation of the resinous material into film structures. It has been found that when poly(para-tertiary-butyl styrene) is blended with polypropylene resin in the aforedescribed additive level amounts, it substantially lowers the minimum heat-seal temperature of such oriented polypropylene film products and, additionally, the additive containing oriented film exhibits improved tensile modulus, i.e. stiffness, which improves the processability of such oriented film material on automatic packaging equipment.

2. Description of the Prior Art In the past, attempts to remedy the hereinbefore discussed defects of oriented polypropylene film, and specifically efforts to improve the heat-seal characteristics and increase the heatseal range thereof, have included the application of various types of coatings to the oriented film surface such as, for example, vinylidene chloride polymers and multipolymers. Although in some instances, such coating application resulted in an oriented film which exhibited satisfactory heat-seal properties, such coating techniques are time consuming and costly, involving the formulation of special coating materials, treatment of the film surface to be coated utilizing, for example, electronic treatment, and in some instances even priming of the treated film surface with material such as, for example, polyethyleneimine to insure adequate adhesion of the topcoating to the oriented film substrate. In many instances such polymer coatings have deleterious effects on the final coated film product such as resulting in the coated film exhibiting poor blocking characteristics.

Other prior art attempts to improve the heat-seal characteristic of oriented polypropylene films include the employment of various additive materials, which, when incorporated in the polypropylene resin prior to conversion thereof into an oriented film structure, are intended to improve the heat-seal characteristics of the film. US. Pat. Nos. 3,313,754 and 3,463,752 are characteristic of the prior art disclosures relating to the employment of additives to improve the properties of oriented polypropylene films. Applicant has found that when prior art additives such as those described in the prior art are employed to alter the oriented film properties, undesirable effects are obtained in the final film, such as film discoloration and a higher coefficient of friction for example. Also, it has been found that certain prior art film additives will increase the blocking tendency of oriented films.

SUMMARY OF THE INVENTION In accordance with the present invention resinous compositions are provided which may be employed in the fabrication of oriented polypropylene film which exhibits lower heat seal temperatures, broadened heat-seal temperature ranges and increased tensile modulus when compared to oriented film structures which do not contain applicants modifying additive. The compositions of the present invention comprise polypropylene resin containing additive amounts, on the order of from about 10 per cent up to about 40 per cent by weight, based upon the total weight of polypropylene resin, of poly( para-tertiary-butyl styrene).

DESCRIPTION OF SPECIFIC EMBODIMENTS Varying amounts of a normally solid poly(para-tertiarybutyl styrene) resin identified by the manufacturer as XPR-49, and having the following properties:

Tg (Glass Transition Temperature) 79 C. Respective Index L540 Ash Content 0.00l Elemental Analysis H 10.0 Decomposition Temperature 300 C. Color Water White Softening Point -120" C. Molecular Weight 3010 (Weight Average) Molecular Weight 1520 (Number were admixed with molten polypropylene resin identified by the manufacturer as Eastman Tenite 423DF, a high isotactic content, crystalline polypropylene having the following properties:

Melt Index 4.5

Crystalline Melting Point, F. 330

Inherent Vlscosity 1.4-1.6 Molecular Weight 100,000-120,000 Density (grams/cc.) 0.902

Vicat Softening Point, F. 293

The polypropylene, poly(para-tertiary-butyl styrene) blends were prepared by fluxing the polypropylene resin at 200 C. in a Brabender Plasticorder for 5 minutes to achieve complete melting of the resin. Poly(para-tertiary butyl styrene) is added slowly and the mixture is mixed for 30 minutes under a nitrogen blanket.

Following the compounding procedure hereinabove described, the admixture was molded into plaques approximately 25 mils thick. The individual plaques were biaxially oriented at temperatures within the range of from about 280 F. up to about 310 F., by stretching the plaques about 250 percent in one direction and subsequently stretching the monoaxially oriented plaque, in a direction perpendicular to the first stretch direction, about 600 percent. The final gauge of the additive containing biaxially oriented film samples was about 1 mil.

In the following Table I, various physical properties of the additive containing, biaxially oriented films, produced in accordance with the above-described procedure are given and I compared to a biaxially oriented polypropylene film contain ing no poly(para-tertiary-butyl styrene). The percentage levels of poly(para-tertiary-butyl styrene) additive are expressed as percent by weight based upon the total weight of the additive containing sample.

In the following Table II, the results of a series of heat seal tests were performed on film samples, identical to the samples tested in preceding Table I, are given. The seals were made utilizing pressures of 20 psi. and a dwell time of 0.5 seconds. The values of the heat seals obtained are expressed in grams per linear inch. The heat seals were measured by sealing together two pieces of the additive containing oriented polypropylene film at temperatures indicated in table II. The values given expressed in grams per linear inch represent the force required to separate the sealed film layers at a rate of about 12 inches per minute utilizing a Suter heat seal tester.

TABLE I Percent by weight additive 30% 40% (1) Coefficient of friction .37 .45 .44 v45 45 (2) Haze L0 1.8 1.7 1,5 0.0 (3) Gloss 87.3 87.8 92.6 91.6 91.3 5 (4) Ball Burst, 72 F. (cm.-kg./mil) 10.1 12.9 11.6 9.7 7. 6 (4) Ball Burst, 0 F. (cm.-kg./mil) 11.3 11,2 9. 9 4. 3 4. 0 (5) Modulus, Ml) (MPSI) 272 2GB 296 321 303 (5) Modulus, TD (MPSI) 497 556 545 501 520 (6) Bl0cking (grams per linear inch) .7 .8 1. 2 2. 8

6 *ASTM, test designations: (1) D-189463; (2) D-lOOS-Gl; (3) D-245- 10 TABLE II Seal strengths at Sealing temperature, F- 220 240 260 Percent by weight additive poly (paratertiary-butyl styrene):

As shown, in preceding Table II, the film samples which contained no additive had extremely poor heat seal values at seal temperatures which produced excellent seal values for the poly(para-tertiary-butyl styrene) containing film samples of the present invention. When attempts were made to obtain satisfactory heat seals on the oriented polypropylene film containing no additive, by increasing the heat seal temperature to about 290 F., the film shrank and tore as a result of the disorientation caused by such an elevated temperature.

Although the present invention has been described with preferred embodiments, it is to be understood that modifications and variations may be resorted to, without departing from the spirit and scope of this invention, as those skilled in the art will readily understand. Such variations and modifications are considered to be within the purview and scope of the appended claims.

What is claimed is:

l. A thermoplastic resin composition comprising a mixture of an essentially isotactic, crystalline polypropylene containing from about 10 percent up to about 40 percent by weight, based upon the total weight of said mixture, of poly(para-tertiarybutyl styrene).

2. Oriented polypropylene film containing additive amounts of from about 10 percent to about 40 percent by weight of poly( para-tertiary-butyl styrene PO-IOSO Patent No. 3 Dated May 972 Inventofls) Edward rd It is certified that error appears in the above-identified parent and that said Letters Patent are hereby corrected as shown below:

Column 2, line 2 L, Change "(Number" to --(Nu1nber Average)-- Signed and sealed this 23rd day of January 1973.

(SEAL) Attest:

ROBERT GOTTSCHALK EDWARD MrFLETCHER IR. Attesting Officer Commissioner of Patents 

2. Oriented polypropylene film containing additive amounts of from about 10 percent to about 40 percent by weight of poly(para-tertiary-butyl styrene). 